Procedure: | |||
0.5 g of 22000g/mol PVOH was added to 3mL of water and stirred with heat until dissolved (~15 minutes). In addition to this 3 other solutions containing the following were prepared under the same procedure: 1.0g of 22000g/mol PVOH in 5mL H2O and 0.5g and 1.0g 100000g/mol PVOH in 3mL and 5mL H2O respectively. Once all four solutions were prepared, each was poured into a round dish where they were left to dry for 48 hours. | |||
==Data== | ==Data== |
Revision as of 07:50, 12 September 2012
Experimental Chemistry | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
ObjectiveSynthesize 4 thin films using polyvinyl alcohols of different molecular weights DescriptionProcedure: 0.5 g of 22000g/mol PVOH was added to 3mL of water and stirred with heat until dissolved (~15 minutes). In addition to this 3 other solutions containing the following were prepared under the same procedure: 1.0g of 22000g/mol PVOH in 5mL H2O and 0.5g and 1.0g 100000g/mol PVOH in 3mL and 5mL H2O respectively. Once all four solutions were prepared, each was poured into a round dish where they were left to dry for 48 hours. Data
NotesThis area is for any observations or conclusions that you would like to note.
|