In addition to this, the solubility of previously synthesized thin films were tested. 0.2g of the following films (MW=22000) were placed in water with stirring to observe if completely soluble: | In addition to this, the solubility of previously synthesized thin films were tested. 0.2g of the following films (MW=22000) were placed in water with stirring to observe if completely soluble: | ||
A. 0.5g PVOH | A. 0.5g PVOH | ||
B. 0.5gPVOH/ | |||
C. 0.5g PVOH/ | B. 0.5gPVOH/H<sub>3</sub>PO<sub>4</sub> | ||
C. 0.5g PVOH/H<sub>3</sub>PO<sub>4</sub>/Maleic Acid | |||
0.2g of A-C polymers were cross linked by placing in the oven for ~90 minutes allowing for dehydration to occur. The solubility of these films were also tested and results were compared to that of the non-cross linked polymer samples. | 0.2g of A-C polymers were cross linked by placing in the oven for ~90 minutes allowing for dehydration to occur. The solubility of these films were also tested and results were compared to that of the non-cross linked polymer samples. | ||
Revision as of 12:38, 5 October 2012
 Experimental Chemistry
|
<html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
|
ObjectivePrepare thin films suitable for IR Spectroscopy Analysis, test solubility of PVOH thin films, perform cross-linking experiment on thin films Description0.1g of PVOH (MW=22000 AND MW=100000) was dissolved in ~5-6mL of water and dried to be used in IR analysis. In addition to this, the solubility of previously synthesized thin films were tested. 0.2g of the following films (MW=22000) were placed in water with stirring to observe if completely soluble: A. 0.5g PVOH B. 0.5gPVOH/H3PO4 C. 0.5g PVOH/H3PO4/Maleic Acid 0.2g of A-C polymers were cross linked by placing in the oven for ~90 minutes allowing for dehydration to occur. The solubility of these films were also tested and results were compared to that of the non-cross linked polymer samples. DataEach of the non-cross linked samples were completely soluble in water. After cross linkage, however, there were differences in solubility. Both A and B completely dissolved, C did not dissolve. NotesN/A
| |