User:Allison K. Alix/Notebook/CHEM-581/2012/09/07: Difference between revisions
(Autocreate 2012/09/07 Entry for User:Allison_K._Alix/Notebook/CHEM-581) |
(fix raw html notebook nav) |
||
(9 intermediate revisions by one other user not shown) | |||
Line 2: | Line 2: | ||
|- | |- | ||
|style="background-color: #EEE"|[[Image:BDLlogo_notext_lr.png|128px]]<span style="font-size:22px;"> Experimental Chemistry</span> | |style="background-color: #EEE"|[[Image:BDLlogo_notext_lr.png|128px]]<span style="font-size:22px;"> Experimental Chemistry</span> | ||
|style="background-color: #F2F2F2" align="center"| | |style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]] }}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}} | ||
|- | |- | ||
| colspan="2"| | | colspan="2"| | ||
Line 10: | Line 10: | ||
==Objective== | ==Objective== | ||
Prepare thin films suitable for IR Spectroscopy Analysis, test solubility of PVOH thin films, perform cross-linking experiment on thin films | |||
==Description== | ==Description== | ||
0.1g of PVOH (MW=22000 AND MW=100000) was dissolved in ~5-6mL of water and dried to be used in IR analysis. | |||
= | In addition to this, the solubility of previously synthesized thin films were tested. 0.2g of the following films (MW=22000) were placed in water with stirring to observe if completely soluble: | ||
A. 0.5g PVOH | |||
B. 0.5gPVOH/H<sub>3</sub>PO<sub>4</sub> | |||
C. 0.5g PVOH/H<sub>3</sub>PO<sub>4</sub>/Maleic Acid | |||
0.2g of A-C polymers were cross linked by placing in the oven for ~90 minutes allowing for dehydration to occur. The solubility of these films were also tested and results were compared to that of the non-cross linked polymer samples. | |||
==Data== | |||
Each of the non-cross linked samples were completely soluble in water. After cross linkage, however, there were differences in solubility. Both A and B completely dissolved, C did not dissolve. | |||
==Notes== | |||
N/A | |||
Latest revision as of 21:59, 26 September 2017
Experimental Chemistry | Main project page Previous entry Next entry |
ObjectivePrepare thin films suitable for IR Spectroscopy Analysis, test solubility of PVOH thin films, perform cross-linking experiment on thin films Description0.1g of PVOH (MW=22000 AND MW=100000) was dissolved in ~5-6mL of water and dried to be used in IR analysis. In addition to this, the solubility of previously synthesized thin films were tested. 0.2g of the following films (MW=22000) were placed in water with stirring to observe if completely soluble: A. 0.5g PVOH B. 0.5gPVOH/H3PO4 C. 0.5g PVOH/H3PO4/Maleic Acid 0.2g of A-C polymers were cross linked by placing in the oven for ~90 minutes allowing for dehydration to occur. The solubility of these films were also tested and results were compared to that of the non-cross linked polymer samples. DataEach of the non-cross linked samples were completely soluble in water. After cross linkage, however, there were differences in solubility. Both A and B completely dissolved, C did not dissolve. NotesN/A
|