0.1g of polyvinyl alochol film (0.5 g in 6mL | 0.1g of polyvinyl alochol film (0.5 g in 6mL H<sub>2</sub>O) treated with gluteraldehyde was placed in a solution containing 100mL H<sub>2</sub>O, 2mL HCl, and 20g Na<sub>2</sub>SO<sub>4</sub> @ 70°C. The sodium sulfate is added to decrease solubility of the polymer during the acetalization reaction. The polymer film was immersed in solution with stirring for 1 hour. The film was then rinsed with H<sub>2</sub>O and immersed in a 1% HCl solution @ 70°C for 1/2 hour. It was then transferred to a 0.2M solution of sodium bicarbonate for 15 minutes, to neutralize the HCl from the previous solution. | ||
==Data== | ==Data== |
Revision as of 12:25, 5 October 2012
Experimental Chemistry | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
ObjectiveIn Situ cross-linking of polyvinyl alcohol films Description0.1g of polyvinyl alochol film (0.5 g in 6mL H2O) treated with gluteraldehyde was placed in a solution containing 100mL H2O, 2mL HCl, and 20g Na2SO4 @ 70°C. The sodium sulfate is added to decrease solubility of the polymer during the acetalization reaction. The polymer film was immersed in solution with stirring for 1 hour. The film was then rinsed with H2O and immersed in a 1% HCl solution @ 70°C for 1/2 hour. It was then transferred to a 0.2M solution of sodium bicarbonate for 15 minutes, to neutralize the HCl from the previous solution. Data
NotesSee NASA Technical Paper 1407
|