X-Ray Diffraction Analysis on sodium cloisite sample. Run for ~30 minutes. A solution was prepared using 1.25g copper sulfate in 500mL | X-Ray Diffraction Analysis on sodium cloisite sample. Run for ~30 minutes. A solution was prepared using 1.25g copper sulfate in 500mL H<sub>2</sub>O. In addition to this, 5 serial dilutions of the two solutions prepared on 9/19 were prepared (20 ppm CuSO<sub>4</sub>, 20ppm Na<sub>2</sub>SO<sub>4</sub>) each using 1mL of the previous solution and 9mL of H<sub>2</sub>O. The PVOH films previously synthesized containing 1mL gluteraldehyde were treated using fixant solutions (see 9/19 for solution contents) for 1 hour at 70°C. | ||
==Data== | ==Data== |
Revision as of 12:22, 5 October 2012
Experimental Chemistry | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
ObjectiveDescriptionX-Ray Diffraction Analysis on sodium cloisite sample. Run for ~30 minutes. A solution was prepared using 1.25g copper sulfate in 500mL H2O. In addition to this, 5 serial dilutions of the two solutions prepared on 9/19 were prepared (20 ppm CuSO4, 20ppm Na2SO4) each using 1mL of the previous solution and 9mL of H2O. The PVOH films previously synthesized containing 1mL gluteraldehyde were treated using fixant solutions (see 9/19 for solution contents) for 1 hour at 70°C. Data
NotesThis area is for any observations or conclusions that you would like to note.
|