User:Allison K. Alix/Notebook/CHEM-581/2012/10/03: Difference between revisions

From OpenWetWare
Jump to navigationJump to search
(6 intermediate revisions by the same user not shown)
Line 13: Line 13:


==Description==
==Description==
Dimensional Mechanical Analysis will be performed on previously synthesized PVOH films consisting of the following: 1) MW: 22000 2) MW: 100000 3) MW: 22000 with phosphoric acid 4) MW: 100000 with hydrochloric acid 5) MW: 22000 with phosphoric acid and maleic acid. Samples 3-5 were crosslinked via dehydration in the oven at 120 degrees celsius for 90 minutes. Samples of films 1 and 2 were also cross linked via dehydration for a before and after comparison of crosslinking.
Dimensional Mechanical Analysis (DMA) will be performed on previously synthesized PVOH films consisting of the following:  
 
1) MW: 22000  
 
2) MW: 100000  
 
3) MW: 22000 with phosphoric acid  
 
4) MW: 100000 with hydrochloric acid  
 
5) MW: 22000 with phosphoric acid and maleic acid.  
 
Samples 3-5 were crosslinked via dehydration in the oven at 120°C for 90 minutes. Samples of films 1 and 2 were also cross linked via dehydration for a before and after comparison of crosslinking.


==Data==
==Data==
'''PVOH MW: 22000''' height: 20.49mm width: 0.22mm
<u>PVOH MW: 22000</u>
 
height: 20.49mm  
 
width: 0.22mm.
 
The films that were cross-linked in the oven had some considerable changes in color and toughness:
 
*MW 100,000: film became much tougher, no visible color changes.
*MW 22000: no toughness or color changes.
*MW 22000 w/ phosphoric acid: film became much tougher and turned a slight yellowish brown color.
*MW 22000 with phosphoric acid and maleic acid: no changes in toughness or color.
*MW: 100,000 w/ hydrochloric acid: toughness did not change but color became a very dark black


==Notes==
==Notes==

Revision as of 10:52, 5 October 2012

Experimental Chemistry <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page
<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html>&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;</html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>


Objective

Dynamic Mechanical Analysis of PVOH films

Description

Dimensional Mechanical Analysis (DMA) will be performed on previously synthesized PVOH films consisting of the following:

1) MW: 22000

2) MW: 100000

3) MW: 22000 with phosphoric acid

4) MW: 100000 with hydrochloric acid

5) MW: 22000 with phosphoric acid and maleic acid.

Samples 3-5 were crosslinked via dehydration in the oven at 120°C for 90 minutes. Samples of films 1 and 2 were also cross linked via dehydration for a before and after comparison of crosslinking.

Data

PVOH MW: 22000

height: 20.49mm

width: 0.22mm.

The films that were cross-linked in the oven had some considerable changes in color and toughness:

  • MW 100,000: film became much tougher, no visible color changes.
  • MW 22000: no toughness or color changes.
  • MW 22000 w/ phosphoric acid: film became much tougher and turned a slight yellowish brown color.
  • MW 22000 with phosphoric acid and maleic acid: no changes in toughness or color.
  • MW: 100,000 w/ hydrochloric acid: toughness did not change but color became a very dark black

Notes

A non-cross linked sample of film 1 will have to be re-analyzed as the length was entered as 3.5mm instead of 5.3mm