== | ==Objective== | ||
* | # Continue processing films from last week | ||
# Make two new films | |||
## One containing the exchanged clay that your group made | |||
###0.9995g of PVA with 0.1107g of 1-hexadecyltriphenylphosphonium bromide | |||
## One containing the exchanged clay that another group made | |||
###1.0022g of PVA with 0.1111g of tributylhexadecylphosphonium bromide used from [[User:Michael_S._Bible/Notebook/581|Michael's]] group | |||
==Data== | |||
====PVA films soaked in R6G==== | |||
{| {{table}} | |||
| align="center" style="background:#f0f0f0;"|'''PVA''' | |||
| align="center" style="background:#f0f0f0;"|'''Concentration (micromL)''' | |||
| align="center" style="background:#f0f0f0;"|'''Mass of Vial (g)''' | |||
| align="center" style="background:#f0f0f0;"|'''Mass of Vial and Film (g)''' | |||
| align="center" style="background:#f0f0f0;"|'''Mass of Film (g)''' | |||
|- | |||
| 1||1||16.4096||16.5057||0.0961 | |||
|- | |||
| 2||10||16.5198||16.6298||0.11 | |||
|- | |||
| 3||20||16.3885||16.5115||0.123 | |||
|- | |||
| | |||
|} | |||
PVAC films soaked in R6G | |||
{| {{table}} | |||
| align="center" style="background:#f0f0f0;"|'''PVAC''' | |||
| align="center" style="background:#f0f0f0;"|'''Concentration (micromL)''' | |||
| align="center" style="background:#f0f0f0;"|'''Mass of Vial (g)''' | |||
| align="center" style="background:#f0f0f0;"|'''Mass of Vial and Film (g)''' | |||
| align="center" style="background:#f0f0f0;"|'''Mass of Film (g)''' | |||
|- | |||
| 4||1||16.3905||16.4411||0.0506 | |||
|- | |||
| 5||10||16.3518||16.4301||0.0783 | |||
|- | |||
| 6||20||16.3959||16.4812||0.0853 | |||
|- | |||
| | |||
|} | |||
====Preparation of solutions==== | |||
* Stock solution was 159uM | |||
#1uM R6G - 12.578mL of stock into 100mL | |||
#10uM R6G - 6.289 mL of stock into 100mL | |||
#20uM R6G - 0.629 mL of stock into 100mL | |||
Revision as of 07:34, 24 September 2014
Project name | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> | ||||||||||||||||||||||||||||||||||||||||||
Objective
DataPVA films soaked in R6G
PVAC films soaked in R6G
Preparation of solutions
|