User:Elizabeth Ghias/Notebook/Experimental Chemistry/2012/08/31: Difference between revisions
No edit summary |
No edit summary |
||
Line 20: | Line 20: | ||
Film 1 - 0.5110 g PVA in 3 mL water, no acid was added | Film 1 - 0.5110 g PVA in 3 mL water, no acid was added | ||
Film 2 - 0.5053 g PVA in 3 mL water, 2 drops of phosphoric acid was added | Film 2 - 0.5053 g PVA in 3 mL water, 2 drops of phosphoric acid was added | ||
Film 3 - 0.5078 g PVA in 3 mL water, 2 drops of 12 M hydrochloric acid was added | Film 3 - 0.5078 g PVA in 3 mL water, 2 drops of 12 M hydrochloric acid was added | ||
Film 4 - 1.0084 g PVA in 6 mL water, no acid was added | Film 4 - 1.0084 g PVA in 6 mL water, no acid was added | ||
Film 5 - 1.0010 g PVA in 6 mL water, 3 drops of phosphoric acid was added | Film 5 - 1.0010 g PVA in 6 mL water, 3 drops of phosphoric acid was added | ||
Film 6 - 1.0044 g PVA in 6 mL water, 3 drops of 12 M hydrochloric acid was added | Film 6 - 1.0044 g PVA in 6 mL water, 3 drops of 12 M hydrochloric acid was added | ||
<u>Viscosity Tests (Part 1)</u> | |||
# | |||
==Data== | ==Data== |
Revision as of 12:08, 7 September 2012
Experimental Chemistry | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
ObjectiveTo create crosslinked films through acid catalyzed dehydration and to perform viscosity tests. DescriptionFilm Preparation with Acid Dehydration
Film 1 - 0.5110 g PVA in 3 mL water, no acid was added Film 2 - 0.5053 g PVA in 3 mL water, 2 drops of phosphoric acid was added Film 3 - 0.5078 g PVA in 3 mL water, 2 drops of 12 M hydrochloric acid was added Film 4 - 1.0084 g PVA in 6 mL water, no acid was added Film 5 - 1.0010 g PVA in 6 mL water, 3 drops of phosphoric acid was added Film 6 - 1.0044 g PVA in 6 mL water, 3 drops of 12 M hydrochloric acid was added
Data
NotesThis area is for any observations or conclusions that you would like to note.
|