User:Elizabeth Ghias/Notebook/Experimental Chemistry/2012/10/15

Objective

To remake the glutaraldehyde films containing clay, to make a film with porphyrin, and to measure sodium ion content using an ion selective electrode.

Description

Making Glutaraldehyde Films

• 4 films were made - (1)PVOH/glutaraldehyde, (2)PVOH/Na-MT/glutaraldehyde, (3)PVOH/100% CEC Clay/glutaraldehyde, and (4)PVOH/porphyrin/glutaraldehyde

1. Film 1 was made by dissolving 1 g PVOH in 7 mL of water. Once all the PVOH had dissolved, 1 mL of glutaraldehyde was added. The solution was stirred for 5 minutes and then was poured into a dish and allowed to evaporate until Wednesday.
   • Actual amount of PVOH = 1.0059 g
2. Film 2 was made by dissolving 1 g PVOH and 0.1 g Na-MT in 7 mL of water. Once they had dissolved, 1 mL of glutaraldehyde was added. The solution was allowed to mix for 5 minuntes and then was poured into a dish and allowed to evaporate until Wednesday.
   • Actual amount of PVOH = 1.0021 g, actual amount of Na-MT = 0.1016 g
3. Film 3 was made by dissolving 1 g PVOH and 0.1 g 100% CEC clay in 7 mL of water. Once they had dissolved, 1 mL of glutaraldehyde was added. The solution was allowed to stir for 5 minuntes and then was poured into a dish and allowed to evaporate until Wednesday.
   • Actual amount of PVOH added = 1.0014 g, actual amount of 100% CEC clay = 0.1004 g.
4. Film 4 was made by dissolving 1 g PVOH in 7 mL of water. Once it dissolved, 1 mL of glutaraldehyde and 1 mL of porphyrin was added. The solution was allowed to mix for 5 minutes and then was poured into a dish and allowed to evaporate until Wednesday.

Determining the Sodium Ion Content

• The sodium ion content of the filtrates collected on

1. An 0.1 mL of ionic strength adjuster (4M solution containing NaOH) was added to a 3 mL of each solution to be tested, so that the pH of each solution would fall in the range of pH = 8 to 10.
2. The electrode was placed into each of the solutions and were allowed to equilibrate for 2 minutes.

Data

Ion Selective Electrode Results

Notes

• For an ion selective electrode, higher concentrations have more negative voltages.
• The film containing the porphyrin had a light pink color to it.