User:Elizabeth Schott/Notebook/Nanoparticles/2015/05/27: Difference between revisions
| Line 24: | Line 24: | ||
[[Image:NPConcSizCalc22.png|500px]] | [[Image:NPConcSizCalc22.png|500px]] | ||
The first table contains original calculations. The second table contains calculations corrected by baseline data. | The first table contains original calculations.Average size of nanoparticle was approximately 12.75 nm with a standard deviation of 3.5075 nm. The average concentration was approximately 2.46E-08 with a standard deviation of 6.32E-08. | ||
The second table contains calculations corrected by baseline data. Recalculated average size of nanoparticle was 13.65 nm with a standard deviation of 3.43779 nm. The recalculated average concentration (nm/M^-1 cm^-1) was approximately 1.22E-08 with a standard deviation of 8.08E-09. | |||
''Discussion'' | ''Discussion'' | ||
Revision as of 13:47, 27 May 2015
 Project name
|
<html><img src="/images/9/94/Report.png" border="0" /></html> Main project page Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
May 27 2015: Determining Size and Concentration of Au Nanoparticles from UV-Vis SpectraProcedure 1) Spectrometer was set up to laptop, where a blank cuvette filled with water was used to calibrate the system. 2) The cuvette was filled with 1 mL of solution from the sample being tested and 1 mL of water. This was done because the absorbancy level of an undiluted solution exceeded one. This measure was followed for each of the 20 samples, which in turn created 20 diluted samples, which were marked and sealed separately. 3) Raw data was recorded into excel for each of the 20 samples, where size and concentration was determined (see results). 4) The average absorbancy of each raw sample was then base lined using the Gaussian equation on excel, and recalculated to determine size and concentration of the gold nanoparticles (see results)
The first table contains original calculations.Average size of nanoparticle was approximately 12.75 nm with a standard deviation of 3.5075 nm. The average concentration was approximately 2.46E-08 with a standard deviation of 6.32E-08. The second table contains calculations corrected by baseline data. Recalculated average size of nanoparticle was 13.65 nm with a standard deviation of 3.43779 nm. The recalculated average concentration (nm/M^-1 cm^-1) was approximately 1.22E-08 with a standard deviation of 8.08E-09. Discussion
| |