User:Hannah Harvey/Notebook/CHEM-471 Fall 2016/2017/02/14: Difference between revisions
From OpenWetWare
(Autocreate 2017/02/14 Entry for User:Hannah_Harvey/Notebook/CHEM-471_Fall_2016) |
(fix raw html notebook nav) |
||
(8 intermediate revisions by one other user not shown) | |||
Line 2: | Line 2: | ||
|- | |- | ||
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | |style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | ||
|style="background-color: #F2F2F2" align="center"| | |style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]] }}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}} | ||
|- | |- | ||
| colspan="2"| | | colspan="2"| | ||
<!-- ##### DO NOT edit above this line unless you know what you are doing. ##### --> | <!-- ##### DO NOT edit above this line unless you know what you are doing. ##### --> | ||
== | ==Purpose== | ||
* | *To determine if coating the glassy carbon electrode with nanofibers blocked electron transfer. | ||
**15 μL | |||
**20 μL | |||
==Protocol== | |||
'''Electrochemical Analysis''' | |||
*CH Instruments Electrochemical Analyzer was used. | |||
#5 mM hexaammineruthenium(III) chloride and 1M KCl solution was used in electrochemical cell. | |||
#The glassy carbon electrode was cleaned with 0.3 and then 0.05 alumina slurry and then sonicated. | |||
#The reference electrode, the platinum wire, and the GCE were attached to the instrument. | |||
#The parameters were set at: | |||
*Initial: 0.2 | |||
*High: 0.2 | |||
*Low: -0.4 | |||
*Initial Scan: Negative | |||
*Scan Rate: 0.05 | |||
*Segments: 4 | |||
*Sensitivity 1x10^(-5) | |||
*Sample Interval: 0.001 | |||
#Then the instrument was ran. | |||
#This same procedure was with the addition of 15μL or 20μL of nanofibers which had been dropped onto the GCE and allowed to dry. | |||
#The nanofibers had been centrifued at 1300rpm for 1 minute. | |||
*15uL nanofibers take about 40 minutes to dry | |||
'''Nanofiber drying''' | |||
*The fibers were combined in a Petri dish to increase the available drying surface area and let rest overnight. | |||
==Data== | |||
*1M KCl; 15μL Nanofibers; Test 2 | |||
[[Image:Nano 15ul ru hex 5mm - 1 m kcl - sonicated -2.png|600px]]<br/> | |||
'''Figure 1''' dV=.082V dC=8.03*10<sup>-5</sup>A<br/> | |||
*1M KCl; 15μL Nanofibers; Test 3 | |||
[[Image:Nano 15ul ru hex 5mm - 1 m kcl - sonicated -3.png|600px]]<br/> | |||
'''Figure 2''' dV=.083V dC=7.75*10<sup>-5</sup>A<br/> | |||
*1M KCl; 20μL Nanofibers; Test 1 | |||
[[Image:Nano 20ul ru hex 5mm - 1 m kcl - sonicated -1.png|600px]]<br/> | |||
'''Figure 3''' dV=.092V dC=7.75*10<sup>-5</sup>A<br/> | |||
*1M KCl; 20μL Nanofibers; Test 2 | |||
[[Image:Nano 20ul ru hex 5mm - 1 m kcl - sonicated -2.png|600px]]<br/> | |||
'''Figure 4''' dV cannot be determined dC=9.92*10<sup>-5</sup>A<br/> | |||
==Results== | |||
==Notes== | |||
[[User:Cassidy B. Hart/Notebook/CHEM-471: Gold & Silver Nanoparticles/2017/02/14|Cassidy Hart]] | |||
<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### --> | <!-- ##### DO NOT edit below this line unless you know what you are doing. ##### --> |
Latest revision as of 02:13, 27 September 2017
Project name | Main project page Previous entry Next entry |
Purpose
ProtocolElectrochemical Analysis
Nanofiber drying
Data
ResultsNotes |