User:Karlena L. Brown/Notebook/PVOH Research/2012/10/31: Difference between revisions
From OpenWetWare
(fix raw html notebook nav) |
|||
(3 intermediate revisions by one other user not shown) | |||
Line 2: | Line 2: | ||
|- | |- | ||
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> PVOH Research</span> | |style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> PVOH Research</span> | ||
|style="background-color: #F2F2F2" align="center"| | |style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]] }}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}} | ||
|- | |- | ||
| colspan="2"| | | colspan="2"| | ||
Line 28: | Line 28: | ||
==Films Examined using FTIR== | ==Films Examined using FTIR== | ||
'''RECALL FTIR PROCEDURAL PROTOCOL 9/17/12''' | '''RECALL FTIR PROCEDURAL PROTOCOL 9/17/12''' | ||
'''LIST OF FILMS FOR FTIR:''' | |||
{| {{table}} | |||
| align="center" style="background:#f0f0f0;"|'''Films''' | |||
| align="center" style="background:#f0f0f0;"|'''New mass(g)''' | |||
|- | |||
| PVOH(22K) 1.0067g+1mL GA+1mL porphyrin crosslinked||1.7688 | |||
|- | |||
| PVOH(22K)+0.5mL GA+0.104g NaMT crosslinked spun 10 min CuSO4 prepared 10/17/2012||0.9465 | |||
|- | |||
| PVOH(22K)+0.5mLGA+0.99mL porphyrin(no color on film )crosslinked prepared 10/19/2012||1.8045 | |||
|- | |||
| PVOH(22K)+1mL GA+100%CEC crosslinked prepared 10/4/2012||1.3662 | |||
|- | |||
| PVOH(22K)+1mL GA+1mL porphyrin crosslinked prepared 10/24/2012||1.5477 | |||
|- | |||
| PVOH(22K)+0.5mL GA+1mL porphyrin crosslinked prepared 10/24/2012 #2||1.9685 | |||
|- | |||
| PVOH(22K)+0.5mLGA+1mL porphyrin prepared crosslinked 10/26/2012||2.1206 | |||
|- | |||
| PVOH(22K)+0.8wt% GA+100%CEC crosslinked spun 10 min CuSO4 prepared 10/26/2012||1.24 | |||
|- | |||
| PVOH(22K)+0.8wt% GA+50% CEC crosslinked spun 10 min CuSO4 prepared 10/17/2012||1.074 | |||
|} | |||
<br> | |||
[[Image:FTIR.JPG]] | [[Image:FTIR.JPG]] | ||
Latest revision as of 22:17, 26 September 2017
PVOH Research | Main project page Previous entry Next entry | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
OBJECTIVES
Furfural Film Preparation
(PVOH 22K Actual Mass = 1.0029g)
(Furfural Actual Mass = 0.3192g)
Films Examined using FTIRRECALL FTIR PROCEDURAL PROTOCOL 9/17/12 LIST OF FILMS FOR FTIR:
Ion Diffusion & Ion Selective Electrode Film Procedures
Ensure the hole separating the two graduated cylinder columns is completely shielded and covered by the PVOH 22K film Ion Diffusion Film Analysis: Varied Ion SolutionA crosslinked PVOH 22K film containing 1mL glutaldehyde that had been exchanged for 10 min in the CuSO4 solution was used for an Ion Selective Electrode Analysis.
Ion Diffusion Film Analysis: HPLC Grade H2O SolutionA crosslinked PVOH 22K film containing 1mL glutaldehyde that had been exchanged for 10 min in the CuSO4 solution was used for an Ion Selective Electrode Analysis.
Notes
|