User:Karlena L. Brown/Notebook/PVOH Research/2013/02/27

From OpenWetWare

(Difference between revisions)
Jump to: navigation, search
(Hydrogel Pressure Samples Tested)
(Notes)
Line 53: Line 53:
* The pipettes that provided the best fluorescence results for each sample were both the straight plastic pipette and 90° angle bent pipette.
* The pipettes that provided the best fluorescence results for each sample were both the straight plastic pipette and 90° angle bent pipette.
* All samples run maintained a composition incorporating Rhodamine 6G dye
* All samples run maintained a composition incorporating Rhodamine 6G dye
 +
* In comparison, the laponite incorporated hydrogels are squishy, clear, extremely adsorbent, and soft to touch
 +
* The sodium montmorrillonite incorporated hydrogels are hard, dingy, flat, and dull colored (brownish appearance)
 +
* For laponite samples, one can actually see the Rhodamine 6G dye added clearly within each hydrogel sample (reddish pink appearance)
 +
* Also the sodium montmorrillonite samples in most cases began to grow a greenish type mold within the hydrogels
* All samples on 2/27/13 were tested using the bent pipette containing the 90° angle. (See figure listed below)
* All samples on 2/27/13 were tested using the bent pipette containing the 90° angle. (See figure listed below)
Figure 1. Image of bent pipette used for pressure testing
Figure 1. Image of bent pipette used for pressure testing

Revision as of 15:10, 24 March 2013

PVOH Research Main project page
Previous entry      Next entry

OBJECTIVES

  1. Continue fluorescence detection through pressure testing analysis of hydrogel samples (new modifications & better results)

Hydrogel Pressure Samples Tested 2

RECALL HYDROGEL PRESSURE TESTING PROTOCOL ON 2/20/13 & FLUORESCENCE ANALYSIS PROCEDURES ON 2/13/13

Sample Order PVOH vs. Clay Ratio PVOH Type Clay Selection Amount of Hydrogel Used (g)
190:10146K110% CEC NaMT w/ DMHXLBR0.1084
290:10130KNaMT0.1044
350:50146K110% CEC NaMT w/ DMHXLBR0.1092
490:10130K110% CEC Laponite w/ DMHXLBR0.1050
550:50130KNaMT0.1050
690:10130KLaponite0.1015
750:50146K110% CEC Laponite w/ DMHXLBR0.1080
850:50130KLaponite0.1036
990:10130K110% CEC NaMT w/ DMHXLBR0.1011
1050:50130K110% CEC Laponite w/ DMHXLBR0.1036
1190:10130K110% CEC NaMT w/ DMHXLBR0.1011
1290:10146KLaponite0.1026
1350:50130K50% CEC NaMT w/ Bu3HdP+0.1052
1450:50146KLaponite0.1045
1590:10130K50% CEC NaMT w/ Bu3HdP+0.1145

Notes

  • The pipettes that provided the best fluorescence results for each sample were both the straight plastic pipette and 90° angle bent pipette.
  • All samples run maintained a composition incorporating Rhodamine 6G dye
  • In comparison, the laponite incorporated hydrogels are squishy, clear, extremely adsorbent, and soft to touch
  • The sodium montmorrillonite incorporated hydrogels are hard, dingy, flat, and dull colored (brownish appearance)
  • For laponite samples, one can actually see the Rhodamine 6G dye added clearly within each hydrogel sample (reddish pink appearance)
  • Also the sodium montmorrillonite samples in most cases began to grow a greenish type mold within the hydrogels
  • All samples on 2/27/13 were tested using the bent pipette containing the 90° angle. (See figure listed below)

Figure 1. Image of bent pipette used for pressure testing Image:Bent pipette 2 27 13.jpg