1) | |||
a) | |||
*PVOH=0.5 grams + 5ml of water dissolved on hot plate + 1ml of glutaraldehyde | |||
**clear and rather thick compared to without glutaraldehyde | |||
b) | |||
*PVOH~.4 grams + 5ml of water dissolved on hot plate with .1262 g PDMS + glutaraldehyde | |||
** clear and rather thick compared to without glutraraldehyde | |||
2) Na-MT~.1grams (repeating with 50% and 100% CEC surfactant clay) added to 20ml CuSO4*5H20 underfume hood | |||
** for Na-MT clay the filter was covered with green/blue color got darker as the time mixed increase, we believe this is because copper exchanged with the na in the clay | |||
** for 100% exchange filler paper was not as green was still pale brown | |||
3) | |||
a) | |||
*Prepare 1.0g PVOH ~ 1.0058g with .1g Na-MT~.1069g heat to dissolve and get a homogeneous mixture | |||
*remove from hot plate and take under fumehood wear goggles, turn off heat and continue stirring | |||
* added glutaraldehyde without heat just stirring for 3 minutes | |||
* pour in dish | |||
b) | |||
*Prepare 1.0g PVOH with .1g 100% CEC Surfactant Clayto dissolve and get a homogeneous mixture | |||
*remove from hot plate and take under fumehood wear goggles, turn off heat and continue stirring | |||
* added glutaraldehyde without heat just stirring for 3 minutes | |||
* pour in dish | |||
==Notes== | ==Notes== |
Revision as of 09:38, 1 October 2012
Biomaterials Design Lab | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
Objective1) remade glutaraldehyde films with pdms and glutaraldehyde
Descriptionwith glutaraldehyde make sure to wear completely covered goggles on face when handeling
a)
b)
2) Na-MT~.1grams (repeating with 50% and 100% CEC surfactant clay) added to 20ml CuSO4*5H20 underfume hood
3) a)
b)
Data/observations1) a)
b)
2) Na-MT~.1grams (repeating with 50% and 100% CEC surfactant clay) added to 20ml CuSO4*5H20 underfume hood
3) a)
b)
NotesThis area is for any observations or conclusions that you would like to note.
|