User:Klare Lazor/Notebook/Chem-496-001/2012/10/15: Difference between revisions
Klare Lazor (talk | contribs) (→Data) |
Klare Lazor (talk | contribs) (→Data) |
||
Line 58: | Line 58: | ||
##PVOH and 1.0014g | ##PVOH and 1.0014g | ||
##100% surfactant clay .1004g | ##100% surfactant clay .1004g | ||
<u>Making Glutaraldehyde Films</u> | |||
* 4 films were made - (1)PVOH/glutaraldehyde, (2)PVOH/Na-MT/glutaraldehyde, (3)PVOH/100% CEC Clay/glutaraldehyde, and (4)PVOH/porphyrin/glutaraldehyde | |||
# Film 1 was made by dissolving 1 g PVOH in 7 mL of water. Once all the PVOH had dissolved, 1 mL of glutaraldehyde was added. The solution was stirred for 5 minutes and then was poured into a dish and allowed to evaporate until Wednesday. | |||
#* Actual amount of PVOH = 1.0059 g | |||
# Film 2 was made by dissolving 1 g PVOH and 0.1 g Na-MT in 7 mL of water. Once they had dissolved, 1 mL of glutaraldehyde was added. The solution was allowed to mix for 5 minuntes and then was poured into a dish and allowed to evaporate until Wednesday. | |||
#* Actual amount of PVOH = 1.0021 g, actual amount of Na-MT = 0.1016 g | |||
#Film 3 was made by dissolving 1 g PVOH and 0.1 g 100% CEC clay in 7 mL of water. Once they had dissolved, 1 mL of glutaraldehyde was added. The solution was allowed to stir for 5 minuntes and then was poured into a dish and allowed to evaporate until Wednesday. | |||
#* Actual amount of PVOH added = 1.0014 g, actual amount of 100% CEC clay = 0.1004 g. | |||
# Film 4 was made by dissolving 1 g PVOH in 7 mL of water. Once it dissolved, 1 mL of glutaraldehyde and 1 mL of porphyrin was added. The solution was allowed to mix for 5 minutes and then was poured into a dish and allowed to evaporate until Wednesday. | |||
<u>Determining the Sodium Ion Content</u> | |||
* The sodium ion content of the filtrates collected on | |||
# An 0.1 mL of ionic strength adjuster (4M solution containing NaOH) was added to a 3 mL of each solution to be tested, so that the pH of each solution would fall in the range of pH = 8 to 10. | |||
# The electrode was placed into each of the solutions and were allowed to equilibrate for 2 minutes. | |||
# This procedure was done for all of standards | |||
==Notes== | ==Notes== |
Revision as of 09:14, 26 October 2012
Biomaterials Design Lab | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
ObjectiveDescriptionremake control: 1mL control glutaraldehyde and 4 other films remake and 1ml glultaraldehye, as well as 1ml of porphyrin exact amount of water so know concentration of solution.
DataMaking Glutaraldehyde Films 4 films were made:
Actual amount of PVOH = 1.0059 g
Actual amount of PVOH = 1.0021 g, actual amount of Na-MT = 0.1016 g
Actual amount of PVOH added = 1.0014 g, actual amount of 100% CEC clay = 0.1004 g.
NotesThis area is for any observations or conclusions that you would like to note.
|