==Preparation of Exfoliated Film== | ==Preparation of Exfoliated Film== | ||
* | * Notes on Exfoliated Clay taken from Dr. Hartings' entry on [[User:Matt Hartings/Notebook/AU Biomaterials Design Lab/2014/09/12|September 12, 2014]]: | ||
** An exfoliated clay has had all of its layers separated from one another. Instead of having layers in water, you have single sheets of material. This should change the absorption properties of the clay. We are going to test PVA-exfoliated clay materials against the regular PVA-clay material. | |||
** To exfoliate clay, you stir it in water for 24 hours. (Luckily Dr. Fox has done this for us already). | |||
** Given the stock solution of 4% sodium montmorillonite, determine how to make a film such that you make a 10% clay (1g of PVA, ?? of exfoliated clay solution). | |||
** Prepare a crosslinked film with the exfoliated clay in a similar manner to your other films | |||
* It was determined that 2.75 g of the 4% sodium montmorillonite is required to make 10% clay. | |||
* The actual weight of the components added were 0.9996 g of PVA into 2.7756 g of the liquefied, 4% sodium montmorillonite solution to make a 10% wt clay. A volume of 7 mL distilled water was added to the mixture. | |||
* The mixture was left stirring for a week. | * The mixture was left stirring for a week. | ||
Revision as of 23:28, 30 September 2014
Project name | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
Powder Xray diffraction
Preparation of Exfoliated Film
Suspension of PVA films in Malachite Green |