==Synthesis of PVA-clay Beads==
==Synthesis of PVA-clay Beads==
* 0.51520 g PVA + 0.05154 g NaMT in 6 mL 10% HCl.
* 0.51520 g PVA + 0.05154 g NaMT in 6 mL 10% HCl.
* 2 mL of 0.8% glutaraldehyde was added to 20 mL of ethyl acetate. The mixture was stirred at maximum speed on a stirrer.
* 1.5 mL of 0.8% glutaraldehyde was added to 20 mL of ethyl acetate. The mixture was stirred at maximum speed on a stirrer.
* The PVA-clay-HCl solution was added to the ethyl acetate mixture in a drop wise manner.  
* The PVA-clay-HCl solution was added to the ethyl acetate mixture in a drop wise manner.  
* Depending on the conditions, microbeads should form between 2-3 minutes. As soon as the beads are visible, IMMEDIATELY ADD 25 mL of 0.2 M NaHCO<sub>3</sub>. Stir for at least 4 minutes, 15 minutes at most.  
* Depending on the conditions, microbeads should form between 2-3 minutes. As soon as the beads are visible, IMMEDIATELY ADD 25 mL of 0.2 M NaHCO<sub>3</sub>. Stir for at least 4 minutes, 15 minutes at most.  
*  
* Beads will be ready once a clear separation of the water and organic phase is observed. Beads will precipitate to the bottom of the beaker. There will still be some beads left in the organic solvent phase.
* Pour the contents into the falcon tube.
   
   


Revision as of 17:39, 4 November 2014

Project name <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page
<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html>&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;</html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>

Suspension of Synthesized Beads in Malachite Green

  • Beads made from last Friday were suspended in 1 mL 80 ppm malachite green.
80 ppm Malachite Green
PVA-clay beads
PVA-clay beads with 80 ppm Malachite Green at initial addition
PVA-clay beads with 80 ppm Malachite Green after 15 minutes

Synthesis of PVA-clay Beads

  • 0.51520 g PVA + 0.05154 g NaMT in 6 mL 10% HCl.
  • 1.5 mL of 0.8% glutaraldehyde was added to 20 mL of ethyl acetate. The mixture was stirred at maximum speed on a stirrer.
  • The PVA-clay-HCl solution was added to the ethyl acetate mixture in a drop wise manner.
  • Depending on the conditions, microbeads should form between 2-3 minutes. As soon as the beads are visible, IMMEDIATELY ADD 25 mL of 0.2 M NaHCO3. Stir for at least 4 minutes, 15 minutes at most.
  • Beads will be ready once a clear separation of the water and organic phase is observed. Beads will precipitate to the bottom of the beaker. There will still be some beads left in the organic solvent phase.
  • Pour the contents into the falcon tube.