==Hemoglobin Fibers==
 +
I am attempting to make AuNP fibers using several different proteins. First up is the bovine hemoglobin in my lab.
-
==Objective==
+
46mg of Hb in 42.5mL of water (MW of Hb ~64500 g/mol). 16.7uM Hb stock
-
Learn how to maintain an OpenWetWare Notebook.
+
(Note, the final solution was cloudy and brown, indicating that not everything went into solution. Will have to check this parameter later)
-
==Description==
+
16.6mg chloroauric acid hydrate (MW = 339.79) in 20mL of water. 2.44mM stock
-
# Add experimental record here. Include what, how, and why...
+
-
==Data==
+
The following table was used to determine the volumes of water, gold, and Hb to add to each tube.
-
* Add data and results here...
+
-
==Notes==
+
[[Image:20130305 VolumesHbAuNPsynthesis.png|600px]]
-
This area is for any observations or conclusions that you would like to note.
+
 +
The tubes containing these liquids were heated at 80C in an oven for 4 hours.
-
Use categories like tags. Change the "Course" category to the one corresponding to your course. The "Miscellaneous" tag can be used for particular experiments, as instructed by your professor. Please be sure to change or delete this tag as required so that the categories remain well organized.
+
A homogeneous suspension of nanoparticles appeared for ratios from ~30 to ~160. At the ratio 170, fiber formation was observed. Also, in ratios greater than ~50, small aggregates were seen in solution. This could be due to the low solubility of the protein or to minimal fiber formation. Will have to check this.  
-
 
+
-
[[Category:Course]]
+
-
[[Category:Miscellaneous]]
+
 +
Also of note, in the solution with fibers (ratio=170), the fibers were clumpier. They were much clumpier in comparison to the BSA AuNP fibers, which were more linear. Will have to run again and analyze this to see if this is the case. This could be due to the fact that the Hb is not as soluble in solution. I also need to run higher ratios of both BSA and Hb to see where fiber formation stops.

Current revision

Biomaterials Design Lab Main project page
Previous entry      Next entry


Hemoglobin Fibers

I am attempting to make AuNP fibers using several different proteins. First up is the bovine hemoglobin in my lab.

46mg of Hb in 42.5mL of water (MW of Hb ~64500 g/mol). 16.7uM Hb stock (Note, the final solution was cloudy and brown, indicating that not everything went into solution. Will have to check this parameter later)

16.6mg chloroauric acid hydrate (MW = 339.79) in 20mL of water. 2.44mM stock

The following table was used to determine the volumes of water, gold, and Hb to add to each tube.

The tubes containing these liquids were heated at 80C in an oven for 4 hours.

A homogeneous suspension of nanoparticles appeared for ratios from ~30 to ~160. At the ratio 170, fiber formation was observed. Also, in ratios greater than ~50, small aggregates were seen in solution. This could be due to the low solubility of the protein or to minimal fiber formation. Will have to check this.

Also of note, in the solution with fibers (ratio=170), the fibers were clumpier. They were much clumpier in comparison to the BSA AuNP fibers, which were more linear. Will have to run again and analyze this to see if this is the case. This could be due to the fact that the Hb is not as soluble in solution. I also need to run higher ratios of both BSA and Hb to see where fiber formation stops.