User:Matt Hartings/Notebook/AU Biomaterials Design Lab/2013/03/05: Difference between revisions
No edit summary |
(fix raw html notebook nav) |
||
| (2 intermediate revisions by one other user not shown) | |||
| Line 2: | Line 2: | ||
|- | |- | ||
|style="background-color: #EEE"|[[Image:BDLlogo_notext_lr.png|128px]]<span style="font-size:22px;"> Biomaterials Design Lab</span> | |style="background-color: #EEE"|[[Image:BDLlogo_notext_lr.png|128px]]<span style="font-size:22px;"> Biomaterials Design Lab</span> | ||
|style="background-color: #F2F2F2" align="center"| | |style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]] }}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}} | ||
|- | |- | ||
| colspan="2"| | | colspan="2"| | ||
| Line 19: | Line 19: | ||
The following table was used to determine the volumes of water, gold, and Hb to add to each tube. | The following table was used to determine the volumes of water, gold, and Hb to add to each tube. | ||
[[Image:20130305 VolumesHbAuNPsynthesis.png| | [[Image:20130305 VolumesHbAuNPsynthesis.png|600px]] | ||
The tubes containing these liquids were heated at 80C in an oven for 4 hours. | The tubes containing these liquids were heated at 80C in an oven for 4 hours. | ||
A homogeneous suspension of nanoparticles appeared for ratios from ~30 to ~160. At the ratio 170, fiber formation was observed. Also, in ratios greater than ~50, small aggregates were seen in solution. This could be due to the low solubility of the protein or to minimal fiber formation. Will have to check this. | A homogeneous suspension of nanoparticles appeared for ratios from ~30 to ~160. At the ratio 170, fiber formation was observed. Also, in ratios greater than ~50, small aggregates were seen in solution. This could be due to the low solubility of the protein or to minimal fiber formation. Will have to check this. | ||
Also of note, in the solution with fibers (ratio=170), the fibers were clumpier. They were much clumpier in comparison to the BSA AuNP fibers, which were more linear. Will have to run again and analyze this to see if this is the case. This could be due to the fact that the Hb is not as soluble in solution. I also need to run higher ratios of both BSA and Hb to see where fiber formation stops. | |||
Latest revision as of 22:31, 26 September 2017
 Biomaterials Design Lab
|
 Main project page Previous entry Next entry
|
|
Hemoglobin FibersI am attempting to make AuNP fibers using several different proteins. First up is the bovine hemoglobin in my lab. 46mg of Hb in 42.5mL of water (MW of Hb ~64500 g/mol). 16.7uM Hb stock (Note, the final solution was cloudy and brown, indicating that not everything went into solution. Will have to check this parameter later) 16.6mg chloroauric acid hydrate (MW = 339.79) in 20mL of water. 2.44mM stock The following table was used to determine the volumes of water, gold, and Hb to add to each tube.
The tubes containing these liquids were heated at 80C in an oven for 4 hours. A homogeneous suspension of nanoparticles appeared for ratios from ~30 to ~160. At the ratio 170, fiber formation was observed. Also, in ratios greater than ~50, small aggregates were seen in solution. This could be due to the low solubility of the protein or to minimal fiber formation. Will have to check this. Also of note, in the solution with fibers (ratio=170), the fibers were clumpier. They were much clumpier in comparison to the BSA AuNP fibers, which were more linear. Will have to run again and analyze this to see if this is the case. This could be due to the fact that the Hb is not as soluble in solution. I also need to run higher ratios of both BSA and Hb to see where fiber formation stops.
| |