== | ==AuNPs== | ||
Prepping some BSA-AuNPs for two purposes | |||
# Samples for TEM at the USNaval Academy | |||
# Samples for Stephanie to use on Friday | |||
Making three samples with a Au:BSA ratio of 90 (colloidal solution) and three with a Au:BSA ratio of 170 (fibers). | |||
= | 7.4mg HAuCl<sub>4</sub>-3H<sub>2</sub>O (MM = 393.83g/mol) in 7.5mL of water (2.5mM) | ||
= | 10mg of BSA (MM = 66776g/mol) in 10mL of water (15uM) | ||
Au:BSA=90 samples | |||
1mL of Au solution, 1.85mL of BSA solution, 7.15mL of water | |||
Au:BSA=170 samples | |||
1mL of Au solution, 0.98mL of BSA solution, 8.02mL of water | |||
In oven at 80C for 4 hours (start at 10:30 am) | |||
Revision as of 08:41, 26 June 2013
 Biomaterials Design Lab
|
<html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
|
AuNPsPrepping some BSA-AuNPs for two purposes
Making three samples with a Au:BSA ratio of 90 (colloidal solution) and three with a Au:BSA ratio of 170 (fibers). 7.4mg HAuCl4-3H2O (MM = 393.83g/mol) in 7.5mL of water (2.5mM) 10mg of BSA (MM = 66776g/mol) in 10mL of water (15uM) Au:BSA=90 samples 1mL of Au solution, 1.85mL of BSA solution, 7.15mL of water Au:BSA=170 samples 1mL of Au solution, 0.98mL of BSA solution, 8.02mL of water In oven at 80C for 4 hours (start at 10:30 am)
| |