User:Megan L. Channell/Notebook/Masters Research/2013/10/24: Difference between revisions
From OpenWetWare
No edit summary |
(fix raw html notebook nav) |
||
(2 intermediate revisions by one other user not shown) | |||
Line 2: | Line 2: | ||
|- | |- | ||
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | |style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | ||
|style="background-color: #F2F2F2" align="center"| | |style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]] }}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}} | ||
|- | |- | ||
| colspan="2"| | | colspan="2"| | ||
Line 15: | Line 15: | ||
##1.0 % - 0.9904 g PLA, 0.0099 g MOF-5, 10 mL dichloromethane | ##1.0 % - 0.9904 g PLA, 0.0099 g MOF-5, 10 mL dichloromethane | ||
##5.0 % - 0.9497 g PLA, 0.0495 g MOF-5, 10 mL dichloromethane | ##5.0 % - 0.9497 g PLA, 0.0495 g MOF-5, 10 mL dichloromethane | ||
##10.0 % - 0.9000 g PLA, 0.9899 g MOF-5, 10 mL dichloromethane | ##10.0 % - 0.9000 g PLA, 0.9899 g MOF-5, 10 mL dichloromethane | ||
##0 % - 0.999 g PLA, 10 mL dichloromethane | ##0 % - 0.999 g PLA, 10 mL dichloromethane | ||
# | #Used the ultrasonic to mix each sample in a plastic vial until dissolved completely. | ||
#Once dissolved, poured into molds to set. | #Once dissolved, poured into molds to set. | ||
==Note== | |||
The 10% is not 10% because there was too much MOF-5. This needs to be re-done. | |||
<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### --> | <!-- ##### DO NOT edit below this line unless you know what you are doing. ##### --> | ||
|} | |} | ||
__NOTOC__ | __NOTOC__ |
Latest revision as of 23:30, 26 September 2017
Project name | Main project page Previous entry Next entry |
PLA Film
Protocol
NoteThe 10% is not 10% because there was too much MOF-5. This needs to be re-done. |