==Au/BSA Fibers==
==Au/BSA Fibers==
* Protocol for Resuspending Au/BSA Fibers
* Protocol for Resuspending Au/BSA Fibers
-
*# Au/BSA solutions were centrifuged at 3000 rpm, 25°C, for 5 min, such that the fibers formed a pellet at the bottom of the centrifuge tube.
+
*# Au/BSA solutions made on [[User:Abigail_E._Miller/Notebook/CHEM571_Lab_Project/2012/08/31|2012/08/31 by Dr. Miller]] were obtained.
 +
*# The solutions were centrifuged at 3000 rpm, 25°C, for 5 min, such that the fibers formed a pellet at the bottom of the centrifuge tube.
*# 1 mL of 10 mM pH 8 Tris buffer was added to each pellet and pipetted up and down to resuspend the fibers.
*# 1 mL of 10 mM pH 8 Tris buffer was added to each pellet and pipetted up and down to resuspend the fibers.
*# Step two was repeated with Tris buffer at concentrations of 1 mM, 100 μM, and 10 μM on fibers with arbitrary Au/BSA mole ratios.
*# Step two was repeated with Tris buffer at concentrations of 1 mM, 100 μM, and 10 μM on fibers with arbitrary Au/BSA mole ratios.
Line 28: Line 29:
* UV-vis spectroscopy was conducted on the resuspended fiber solutions.
* UV-vis spectroscopy was conducted on the resuspended fiber solutions.
 +
* The AuNP/BSA solution ratios were considered arbitrary for this analysis, as the objective was to determine only whether AuNP/BSA fibers could be resuspended in Tris buffer.  The presence of a peak at around 540 nm indicated the presence of AuNPs and therefore successful resuspension of the fibers.
==UV-Vis Analysis==
==UV-Vis Analysis==
Line 33: Line 35:
* Absorbance of AuNP/BSA fibers resuspended in Tris buffer at concentrations of 100 μM, 10 μM, 1 mM, and 10 mM and pH of 8 or 10.
* Absorbance of AuNP/BSA fibers resuspended in Tris buffer at concentrations of 100 μM, 10 μM, 1 mM, and 10 mM and pH of 8 or 10.
* The presence of a peak at around 540 nm for all solutions indicates that at least some AuNPs became resuspended in solution.  However, as no absorbance spectra of pure Tris buffer has been taken, it may be that the peaks are a result of absorbance by the buffer.
* The presence of a peak at around 540 nm for all solutions indicates that at least some AuNPs became resuspended in solution.  However, as no absorbance spectra of pure Tris buffer has been taken, it may be that the peaks are a result of absorbance by the buffer.
 +
** Please refer to the entry on [[User:Melissa_Novy/Notebook/CHEM-571/2012/09/26|2012/09/26]] for UV-vis spectra of Tris buffers and data analysis.
==Notes==
==Notes==

Current revision

Search this Project

Customize your entry pages

Objectives

  • Prepare serial dilutions of 0.1 M Tris buffer stock solution at the following concentrations: 10 mM, 1 mM, 100 μM, 10 μM.
  • Remake Au and BSA stock solutions to check for contamination.
  • Resuspend Au/BSA fibers in different concentrations of pH 8 or 10 Tris buffer.

Au/BSA Fibers

  • Protocol for Resuspending Au/BSA Fibers
    1. Au/BSA solutions made on 2012/08/31 by Dr. Miller were obtained.
    2. The solutions were centrifuged at 3000 rpm, 25°C, for 5 min, such that the fibers formed a pellet at the bottom of the centrifuge tube.
    3. 1 mL of 10 mM pH 8 Tris buffer was added to each pellet and pipetted up and down to resuspend the fibers.
    4. Step two was repeated with Tris buffer at concentrations of 1 mM, 100 μM, and 10 μM on fibers with arbitrary Au/BSA mole ratios.
    5. Steps 2 and 3 were repeated with pH 10 Tris buffer.
  • UV-vis spectroscopy was conducted on the resuspended fiber solutions.
  • The AuNP/BSA solution ratios were considered arbitrary for this analysis, as the objective was to determine only whether AuNP/BSA fibers could be resuspended in Tris buffer. The presence of a peak at around 540 nm indicated the presence of AuNPs and therefore successful resuspension of the fibers.

UV-Vis Analysis

Image:9-5-12_Absorbance_AuNP-BSA_Tris_Buffer.JPG

  • Absorbance of AuNP/BSA fibers resuspended in Tris buffer at concentrations of 100 μM, 10 μM, 1 mM, and 10 mM and pH of 8 or 10.
  • The presence of a peak at around 540 nm for all solutions indicates that at least some AuNPs became resuspended in solution. However, as no absorbance spectra of pure Tris buffer has been taken, it may be that the peaks are a result of absorbance by the buffer.
    • Please refer to the entry on 2012/09/26 for UV-vis spectra of Tris buffers and data analysis.

Notes

  • Please refer to Keyun Wang's entry for observations on making and centrifuging Au/BSA solutions.
  • Please refer to Dhea Patel's entry for volumes and calculations used in remaking the Au/BSA solutions.