User:Melissa Novy/Notebook/CHEM-572/2013/02/19

From OpenWetWare

(Difference between revisions)
Jump to: navigation, search
(PLA2002D Films)
(5 intermediate revisions not shown.)
Line 16: Line 16:
==Objectives==
==Objectives==
 +
* Grind 100Ag-LMT made on [[User:Melissa_Novy/Notebook/CHEM-572/2013/02/05|2013/02/05]] into a fine powder.
* Make PLA2002D + 5 wt% 100Ag-LMT film.
* Make PLA2002D + 5 wt% 100Ag-LMT film.
* Make PLA2002D + 5 wt% LMT film.
* Make PLA2002D + 5 wt% LMT film.
 +
 +
==PLA2002D Films==
 +
* The protocol on [[User:Melissa_Novy/Notebook/CHEM-572/2013/02/06|2013/02/06]] was used to make the films.
 +
* Each film contained 5 wt% of 100Ag-LMT or LMT for one gram of PLA2002D.
 +
<br>
 +
 +
* PLA2002D + 5 wt% LMT film
 +
** Theoretical mass PLA2002D: 1 g
 +
** Theoretical mass LMT: 0.05 g
 +
** Actual mass PLA2002D: 1.009185 g
 +
** Actual mass LMT: 0.05060 g
 +
<br>
 +
 +
* PLA2002D + 5 wt% [[User:Melissa_Novy/Notebook/CHEM-572/2013/02/05|100Ag-LMT]] film
 +
** Theoretical mass PLA2002D: 1 g
 +
** Theoretical mass 100Ag-LMT: 0.05 g
 +
** Actual mass PLA2002D: 1.01686 g
 +
** Actual mass 100Ag-LMT: 0.05062 g
 +
** Final mass of PLA2002D + 5 wt% 100Ag-LMT: 0.97 g
 +
<br>
 +
 +
* Actual content of silver in 0.5 g PLA2002D + 5 wt% 100Ag-LMT:
 +
** Please refer to the entries on [[User:Melissa_Novy/Notebook/CHEM-572/2013/02/05|2013/02/05]] and [[User:Melissa_Novy/Notebook/CHEM-572/2013/02/13|2013/02/13]] for the data listed below.
 +
<br>
 +
 +
  '''0.00622 g AgNO<sub>3</sub> × (1 mol AgNO<sub>3</sub>/169.87 g AgNO<sub>3</sub>) × (1 mol Ag<sup>+</sup>/1 mol AgNO<sub>3</sub>) = 3.66 × 10<sup>-5</sup> mol Ag<sup>+</sup>'''
 +
  '''[Ag<sup>+</sup>] in 5 mL 100Ag-LMT filtrate was 0.000253614 M'''
 +
  '''0.000253614 M Ag<sup>+</sup> × 0.005 L = 1.2681 × 10<sup>-6</sup> mol Ag<sup>+</sup>'''
 +
  '''Therefore, 3.66 × 10<sup>-5</sup> mol Ag<sup>+</sup> − 1.2681 × 10<sup>-6</sup> mol Ag<sup>+</sup> = 3.53 × 10<sup>-5</sup> mol Ag<sup>+</sup> was exchanged into 100Ag-LMT.'''
 +
<br>
 +
 +
  '''0.05 × 0.5 g PLA2002D + 5 wt% 100Ag-LMT = 0.025 g 100Ag-LMT
 +
  '''(3.53 × 10<sup>-5</sup> mol Ag<sup>+</sup>) ÷ (0.05062 g 100Ag-LMT) = x mol Ag<sup>+</sup> ÷ (0.025 g 100Ag-LMT)'''
 +
  '''4.47 × 10<sup>-8</sup>mol Ag<sup>+</sup> in 0.025 g 100Ag-LMT of 0.5 g PLA2002D + 5 wt% 100Ag-LMT film'''
<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### -->
<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### -->
-
|}
+
 
__NOTOC__
__NOTOC__

Revision as of 13:21, 20 February 2013

Search this Project

Customize your entry pages

Objectives

  • Grind 100Ag-LMT made on 2013/02/05 into a fine powder.
  • Make PLA2002D + 5 wt% 100Ag-LMT film.
  • Make PLA2002D + 5 wt% LMT film.

PLA2002D Films

  • The protocol on 2013/02/06 was used to make the films.
  • Each film contained 5 wt% of 100Ag-LMT or LMT for one gram of PLA2002D.


  • PLA2002D + 5 wt% LMT film
    • Theoretical mass PLA2002D: 1 g
    • Theoretical mass LMT: 0.05 g
    • Actual mass PLA2002D: 1.009185 g
    • Actual mass LMT: 0.05060 g


  • PLA2002D + 5 wt% 100Ag-LMT film
    • Theoretical mass PLA2002D: 1 g
    • Theoretical mass 100Ag-LMT: 0.05 g
    • Actual mass PLA2002D: 1.01686 g
    • Actual mass 100Ag-LMT: 0.05062 g
    • Final mass of PLA2002D + 5 wt% 100Ag-LMT: 0.97 g


  • Actual content of silver in 0.5 g PLA2002D + 5 wt% 100Ag-LMT:


  0.00622 g AgNO3 × (1 mol AgNO3/169.87 g AgNO3) × (1 mol Ag+/1 mol AgNO3) = 3.66 × 10-5 mol Ag+
  [Ag+] in 5 mL 100Ag-LMT filtrate was 0.000253614 M
  0.000253614 M Ag+ × 0.005 L = 1.2681 × 10-6 mol Ag+
  Therefore, 3.66 × 10-5 mol Ag+ − 1.2681 × 10-6 mol Ag+ = 3.53 × 10-5 mol Ag+ was exchanged into 100Ag-LMT.


  0.05 × 0.5 g PLA2002D + 5 wt% 100Ag-LMT = 0.025 g 100Ag-LMT
  (3.53 × 10-5 mol Ag+) ÷ (0.05062 g 100Ag-LMT) = x mol Ag+ ÷ (0.025 g 100Ag-LMT)
  4.47 × 10-8mol Ag+ in 0.025 g 100Ag-LMT of 0.5 g PLA2002D + 5 wt% 100Ag-LMT film