Line 25: | Line 25: | ||
#6mL solutions were prepared with the mole ratios of ([[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]]/[[AU_Biomaterials_Design_Lab:Materials/BSA|BSA]]) 60, 80, 100, 120, 128, 130, 132, 133, 134, 136, 138, 140, 160, and 170. .6mL of HAuCl<sub>4</sub> stock was added to each tube, so each was 1.5mM HAuCl<sub>4</sub> | #6mL solutions were prepared with the mole ratios of ([[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]]/[[AU_Biomaterials_Design_Lab:Materials/BSA|BSA]]) 60, 80, 100, 120, 128, 130, 132, 133, 134, 136, 138, 140, 160, and 170. .6mL of HAuCl<sub>4</sub> stock was added to each tube, so each was 1.5mM HAuCl<sub>4</sub> | ||
*The formula m<sub>1</sub>v<sub>1</sub>=m<sub>2</sub>v<sub>2</sub> was used to determine how much BSA was needed for mole ratios (BSA/Au) of 60-170 | |||
**15μM*(volume [[AU_Biomaterials_Design_Lab:Materials/BSA|BSA]] stock solution) = (1.5*6) | |||
***0.6mL [[AU_Biomaterials_Design_Lab:Materials/BSA|BSA]] stock solution in each tube | |||
**7720μM*x mL=6mL*(1.5*60μM) | |||
***0.069mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.331 mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*80μM) | |||
***0.093mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.307mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*100μM) | |||
***0.117mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.283mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*120μM) | |||
***0.134mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.266mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*128μM) | |||
***0.149mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.251mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*130μM) | |||
***.152mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.248mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*132μM) | |||
***0.154mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.246mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*133μM) | |||
***0.155mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.245mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*134μM) | |||
***0.156mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.254mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*136μM) | |||
***0.159mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.244mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*138μM) | |||
***0.161mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.242mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*140μM) | |||
***0.163mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.237mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*160μM) | |||
***0.187mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.213mL H<sub>2</sub>O | |||
**7720μM*x mL=6mL*(1.5*170μM) | |||
***0.198mL [[AU_Biomaterials_Design_Lab:Materials/HAuCl4|HAuCl<sub>4</sub>]] stock solution | |||
***5.202mL H<sub>2</sub>O | |||
**The tubes were capped with tin foil and heated at 85°C for 4 hours. | |||
==Results== | ==Results== |
Revision as of 18:55, 6 December 2012
Project name | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
Objective
Procedure
Results
|