User:Michael S. Bible/Notebook/Summer MOF Research/2016/06/02: Difference between revisions

From OpenWetWare
Jump to navigationJump to search
(fix raw html notebook nav)
 
(One intermediate revision by one other user not shown)
Line 2: Line 2:
|-
|-
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span>
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span>
|style="background-color: #F2F2F2" align="center"|<html><img src="/images/9/94/Report.png" border="0" /></html> [[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>[[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]]<html>&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;</html>}}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]]<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>}}
|style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]]&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;}}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}}
|-
|-
| colspan="2"|
| colspan="2"|
Line 15: Line 15:
* 8.75301 g of 20.028% ZIF-8/ABS was extruded and collected.   
* 8.75301 g of 20.028% ZIF-8/ABS was extruded and collected.   


==Notes==
*Significant discoloration was observed in the resulting composite material.  It was also noted that smoke was produced during the mixing process.  This could be indicative of oxidation.  Future ZIF-8 containing compounds should be made under nitrogen. 


<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### -->
<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### -->
|}
|}


__NOTOC__
__NOTOC__

Latest revision as of 01:50, 27 September 2017

Project name Main project page
Previous entry      Next entry

Creating Samples of 10% and 20% ZIF-8 in ABS

  • To begin, 12.0011 g of ABS was added to the compounder at 195°C and 80 RPM.
  • 8.85785 g was extruded.
  • 1.2008 g ZIF-8 and 7.6681 g ABS were added.
  • 0.02529 g unmelted ABS was removed.
  • 7.71074 g of 10.018% ZIF-8/ABS was extruded and collected.
  • To the remaining 4.276 g material in the extruder, 1.9763 g ZIF-8 and 5.7505 g ABS were added.
  • 8.75301 g of 20.028% ZIF-8/ABS was extruded and collected.

Notes

  • Significant discoloration was observed in the resulting composite material. It was also noted that smoke was produced during the mixing process. This could be indicative of oxidation. Future ZIF-8 containing compounds should be made under nitrogen.