Following PVOH Films were Cross-linked: | Following PVOH Films were Cross-linked: | ||
*1)PVOH film, MW of 22,000-placed in an oven set at 120 deg Celsius for 90 mins. | *1) PVOH film, MW of 22,000-placed in an oven set at 120 deg Celsius for 90 mins. | ||
*2)PVOH film, MW of 100,000-placed in an oven set at 120 deg Celsius for 90 mins. | *2) PVOH film, MW of 100,000-placed in an oven set at 120 deg Celsius for 90 mins. | ||
*3)PVOH film, MW of 100,000 cross-linked with HCl-placed in an oven set at 120 deg Celsius for 90 mins. | *3) PVOH film, MW of 100,000 cross-linked with HCl-placed in an oven set at 120 deg Celsius for 90 mins. | ||
*4)PVOH film, MW of 22,000, cross-linked H3PO4-placed in an oven set at 120 deg Celsius for 90 mins. | *4) PVOH film, MW of 22,000, cross-linked H3PO4-placed in an oven set at 120 deg Celsius for 90 mins. | ||
*5)PVOH film, MW of 22,000, cross-linked with maleic acid and H3PO4-placed in an oven set at 120 deg Celsius for 90 mins. | *5) PVOH film, MW of 22,000, cross-linked with maleic acid and H3PO4-placed in an oven set at 120 deg Celsius for 90 mins. | ||
'''DMA Analysis:''' | '''DMA Analysis:''' |
Revision as of 08:58, 8 November 2012
Experimental Chemistry | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
ObjectiveDMA- Dynamic Mechanical Analysis on PVOH films DescriptionFollowing PVOH Films were Cross-linked:
DMA Analysis: PVOH films were subject to stretch( elastic tension ) mechanical analysis to test its mechanical durability.
Data
NotesThis area is for any observations or conclusions that you would like to note.
|