User:Moira M. Esson/Notebook/CHEM-581/2012/09/05: Difference between revisions
From OpenWetWare
(2 intermediate revisions by the same user not shown) | |||
Line 17: | Line 17: | ||
#For each additional 0.5g, add an additional ~2mL of water | #For each additional 0.5g, add an additional ~2mL of water | ||
#Add the wanted weight percent of either maleic or succinic acid | #Add the wanted weight percent of either maleic or succinic acid | ||
#Add ~2 drops of HCl or H<sub>3</sub>PO<sub>4 | #Add ~2 drops of HCl or H<sub>3</sub>PO<sub>4</sub> | ||
#*Note: HCl and H<sub>3</sub>PO<sub>4 are corrosive | #*Note: HCl and H<sub>3</sub>PO<sub>4</sub> are corrosive | ||
#Place on hot plate and heat to 70°C-80°C | #Place on hot plate and heat to 70°C-80°C | ||
#Stir and heat until dissolved(~15 min) | #Stir and heat until dissolved(~15 min) | ||
Line 33: | Line 33: | ||
*An additional 2mL H<sub>2</sub>O was added to each solution (~10 minutes into heating) to aid in the dissolution of PVOH | *An additional 2mL H<sub>2</sub>O was added to each solution (~10 minutes into heating) to aid in the dissolution of PVOH | ||
<br> | <br> | ||
==Viscosity of PVOH (MW 130,000) Stock Solutions== | ==Viscosity of PVOH (MW 130,000) Stock Solutions== | ||
*The General Protocols for both serial dilutions and viscosity described on 08/31 were used | *The General Protocols for both serial dilutions and viscosity described on 08/31 were used | ||
Line 67: | Line 68: | ||
| 4||1.09E-4||35.5||8.14E-4||50|| | | 4||1.09E-4||35.5||8.14E-4||50|| | ||
|} | |} | ||
<br> | |||
'''Viscosity Calculations''' | |||
Viscosity of pure H<sub>2</sub>O at 24.5°C | Viscosity of pure H<sub>2</sub>O at 24.5°C | ||
{| {{table}} | {| {{table}} | ||
Line 157: | Line 161: | ||
* Average time = 960.27 s | * Average time = 960.27 s | ||
<br> | <br> | ||
==Notes== | ==Notes== | ||
*Another film was prepared specifically for IR analysis | *Another film was prepared specifically for IR analysis |
Revision as of 09:37, 16 October 2012
Project name | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
Objectives
PVOH (MW 22,000) FilmsGeneral Protocol:
Viscosity of PVOH (MW 130,000) Stock Solutions
Viscosity of pure H2O at 24.5°C
Notes
|