User:Moira M. Esson/Notebook/CHEM-581/2013/02/08

From OpenWetWare

< User:Moira M. Esson | Notebook | CHEM-581 | 2013 | 02(Difference between revisions)
Jump to: navigation, search
(→Objectives)
Current revision (17:01, 23 February 2013) (view source)
(→Objectives)
 
(2 intermediate revisions not shown.)
Line 7: Line 7:
<!-- ##### DO NOT edit above this line unless you know what you are doing. ##### -->
<!-- ##### DO NOT edit above this line unless you know what you are doing. ##### -->
==Objectives==
==Objectives==
-
# Run DSC on all of the prepared DSC clay samples.
 
-
# Run DSC on the previously prepared PVA-Lamp microspheres.
 
# Prepare another dye stock solution for PVA-clay microspheres to soak it.
# Prepare another dye stock solution for PVA-clay microspheres to soak it.
# Allow the PVA-clay microspheres to absorb dye.
# Allow the PVA-clay microspheres to absorb dye.
Line 27: Line 25:
==Microsphere preparation==
==Microsphere preparation==
*The general protocol described on [[User:Moira_M._Esson/Notebook/CHEM-581/2013/02/06|2013/02/06]] was followed.
*The general protocol described on [[User:Moira_M._Esson/Notebook/CHEM-581/2013/02/06|2013/02/06]] was followed.
-
 
+
==Hydrogel Preparation==
 +
{| {{table}}
 +
| align="center" style="background:#f0f0f0;"|'''Prepared PVA MW 130,000 hydrogels'''
 +
| align="center" style="background:#f0f0f0;"|''''''
 +
| align="center" style="background:#f0f0f0;"|''''''
 +
| align="center" style="background:#f0f0f0;"|''''''
 +
| align="center" style="background:#f0f0f0;"|''''''
 +
|-
 +
| Composition||Amount of PVA(g)||Amount of clay added(g)||Concentration of dye solution added(uM)||Volume of dye solution added(mL)
 +
|-
 +
| 50:50 PVA:110% Lamp||0.4998||0.4998||165||0.0364
 +
|-
 +
| 50:50 PVA:110% NaMT exchange||0.4992||0.4991||165||0.0364
 +
|}
<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### -->
<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### -->
|}
|}
__NOTOC__
__NOTOC__

Current revision

Project name Main project page
Previous entry      Next entry

Objectives

  1. Prepare another dye stock solution for PVA-clay microspheres to soak it.
  2. Allow the PVA-clay microspheres to absorb dye.
  3. Remove soaking hydrogels from water and allow then to absorb dye.
  4. Synthesize more PVA-clay microspheres.
  5. Finish preparing PVA MW 130,000 hydrogels


Dye solution preparation

  • As with the preparation of the PVA-clay hydrogels, Rhodamine 6G will be used as the dye. An internal concentration of 1μM dye will be used.
    • Because of the removal of all liquid from the microspheres, a 1μM stock solution will be prepared. A dilution was used from the previously prepared stock solutions. After allowing the the microspheres to absorb the dye for an extended period of time, the microspheres will be rinsed with hot and cold water to remove any DMSO.

Calculations 

 M1V1=M2V2
 V1=(1μMx25000μL)/(92μM)=271.74μL
  • The use of 25mL will make it so a dilution is not necessary for each microsphere dye soak. The prepared 1μM solution was prepared in a volumetric flask, parafilmed, and stored for subsequent use.


Microsphere preparation

  • The general protocol described on 2013/02/06 was followed.

Hydrogel Preparation

Prepared PVA MW 130,000 hydrogels ' ' ' '
CompositionAmount of PVA(g)Amount of clay added(g)Concentration of dye solution added(uM)Volume of dye solution added(mL)
50:50 PVA:110% Lamp0.49980.49981650.0364
50:50 PVA:110% NaMT exchange0.49920.49911650.0364