User:Moira M. Esson/Notebook/CHEM-581/2013/02/15: Difference between revisions
(8 intermediate revisions by the same user not shown) | |||
Line 62: | Line 62: | ||
<br> | <br> | ||
Spectra: | Spectra: | ||
Figure 1. Diffusion test for 50:50 PVA MW 146,000-186,00: 50% NaMT hydrogel | <br> | ||
Figure 1. Diffusion test fluorescence spectra for 50:50 PVA MW 146,000-186,00: 50% NaMT hydrogel | |||
[[Image:2 hr diffusion test 50 MW 146 50% NaMT correct.png]] | [[Image:2 hr diffusion test 50 MW 146 50% NaMT correct.png]] | ||
<br> | <br> | ||
'''Correction''': The x-axis should be labeled Wavelength(nm). The image will be corrected. | |||
Figure 2. Diffusion test fluorescence spectra for 50:50 PVA MW 146,000-186,000: NaMT hydrogel | |||
<br> | |||
[[Image:2 hr diffusion test 50 MW 146 NaMT.png]] | |||
<br> | |||
Figure 3. Diffusion test fluorescence spectra for 90:10 ratio of PVA MW 146,000-186,000:Lamponite | |||
<br> | |||
[[Image:2 hr diffusion test 90 MW 146 LP.png]] | |||
<br> | |||
Figure 4. Diffusion test fluorescence spectra for a 90:10 ratio of PVA MW 146,000-186,000:NaMT | |||
<br> | |||
[[Image:2hr diffusion test 90 MW 146 NaMT.png]] | |||
<br> | |||
Figure 5. Diffusion test fluorescence spectra for a 90:10 ratio of PVA MW 146,000-186,000:50% NaMT | |||
<br> | |||
[[Image:2hr rhodamine diffusion test 90 MW 146 50% NaMT.png]] | |||
<br> | |||
*'''Correction: The x-axis should be labeled Wavelength(nm). The image will be corrected''' | |||
Observations: | Observations: | ||
*Each of the samples had a very fast diffusion rate. If the spectra are viewed additively for each hydrogel sample, a significant amount of dye leaked out of the hydrogel sample in only 2 hours, in comparison to the hydrogels which remained in distilled H<sub>2</sub>O for one week and had minimal dye diffusion. This indicates that the dye must be added prior to the freeze-thaw crosslinking method. | *Each of the samples had a very fast diffusion rate. If the spectra are viewed additively for each hydrogel sample, a significant amount of dye leaked out of the hydrogel sample in only 2 hours, in comparison to the hydrogels which remained in distilled H<sub>2</sub>O for one week and had minimal dye diffusion. This indicates that the dye must be added prior to the freeze-thaw crosslinking method. | ||
Line 70: | Line 89: | ||
*Comparing the 50:50 ratio of PVA:clay and the 90:10 ratio, the hydrogels with 50:50 ratio had more dye leak out of the hydrogel than the 90:10 ratio. Perhaps indicates a more effective pressure stimuli. | *Comparing the 50:50 ratio of PVA:clay and the 90:10 ratio, the hydrogels with 50:50 ratio had more dye leak out of the hydrogel than the 90:10 ratio. Perhaps indicates a more effective pressure stimuli. | ||
*In the future, when performing the diffusion tests, after taking a sample every fifteen minutes, the sample will be readded to the test beaker rather than discarded. | *In the future, when performing the diffusion tests, after taking a sample every fifteen minutes, the sample will be readded to the test beaker rather than discarded. | ||
<br> | |||
Revision as of 17:14, 7 March 2013
Project name | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> | |||||||||||||||||||||||||
Objectives
Microsphere Preparation
General Protocol:
For a 90:10 ratio: (25mL)(1μM)/(92μM)=0.272mL For a 50:50 ratio: (25mL)(1μM)/(165μM)=0.152mL
Fluorescence
General Protocol:
Observations:
|