User:Moira M. Esson/Notebook/CHEM-581/2013/02/27

From OpenWetWare

(Difference between revisions)
Jump to: navigation, search
(→Pressure tests)
(→Pressure tests)
(One intermediate revision not shown.)
Line 58: Line 58:
<br>
<br>
Figure 2. Fluorescence of all NaMT hydrogel ssmples
Figure 2. Fluorescence of all NaMT hydrogel ssmples
 +
<br>
 +
[[Image:Fluorescence of Rhodamine 6G obtained from pressure tests of NaMT clay containing hydrogels using a bent pipette.png]]
 +
<br>
Figure 3. Fluorescence of all Lamponite hydrogel samples
Figure 3. Fluorescence of all Lamponite hydrogel samples
Figure 4. Fluorescence of all hydrogel samples
Figure 4. Fluorescence of all hydrogel samples
Line 63: Line 66:
[[Image:Bent pipette pressure testing.png]]
[[Image:Bent pipette pressure testing.png]]
<br>
<br>
 +
*'''Correction''': The x-axis should be labeled wavelength(nm). The image will be corrected.

Revision as of 20:38, 7 March 2013

Project name Main project page
Previous entry      Next entry

Objectives

  1. Perform pressure tests on all prepared hydrogels using a bent pipette.
  2. Run fluorescence on the samples obtained from the pressure tests.


Pressure tests

  • Pressure tests were performed on all hydrogels prepared with Rhodamine 6G added.
  • After the sheer pressure test conducted on 2013/02/22, it was determined that a bent pipette and an unmodified pipette would be used to conduct the pressure tests. Each hydrogel will have at least two pressure tests conducted with the hydrogel: one with a bent pipette and the other with an unmodified pipette.
  • All pressure tests were conducted following the general protocol described on 2013/02/22.


Table 1. Pressure testing information for hydrogels using a bent pipette

Sample Order PVOH vs. Clay Ratio PVOH Type Clay Selection Amount of Hydrogel Used (g)
190:10146K110% CEC NaMT w/ DMHXLBR0.1084
290:10130KNaMT0.1044
350:50146K110% CEC NaMT0.1092
490:10130K110% CEC Laponite0.1050
550:50130KNaMT0.1050
690:10130KLaponite0.1015
750:50146K110% CEC Laponite0.1080
850:50130KLaponite0.1036
990:10130K110% CEC NaMT0.1011
1050:50130K110% CEC Laponite0.1036
1190:10130K110% CEC NaMT0.1011
1290:10146KLaponite0.1026
1350:50130K50% CEC NaMT Bu3HdP+0.1052
1450:50146KLaponite0.1045
1590:10130K50% CEC NaMT Bu3HdP+0.1145


Figure 1. Image of bent pipette used for pressure testing Image:Bent pipette 2 27 13.jpg
Figure 2. Fluorescence of all NaMT hydrogel ssmples
Image:Fluorescence of Rhodamine 6G obtained from pressure tests of NaMT clay containing hydrogels using a bent pipette.png
Figure 3. Fluorescence of all Lamponite hydrogel samples Figure 4. Fluorescence of all hydrogel samples
Image:Bent pipette pressure testing.png