User:Moira M. Esson/Notebook/CHEM-581/2013/03/01: Difference between revisions
From OpenWetWare
Line 15: | Line 15: | ||
*All pressure tests were conducted following the general protocol described on [[User:Moira_M._Esson/Notebook/CHEM-581/2013/02/20|2013/02/20]]. | *All pressure tests were conducted following the general protocol described on [[User:Moira_M._Esson/Notebook/CHEM-581/2013/02/20|2013/02/20]]. | ||
*Pressure tests were conducted using an unmodified pipette in order to determine if the very slight amount of sheer pressure caused by an unmodified pipette would cause a detectable amount of dye diffusion. | *Pressure tests were conducted using an unmodified pipette in order to determine if the very slight amount of sheer pressure caused by an unmodified pipette would cause a detectable amount of dye diffusion. | ||
<br> | |||
Table 1. Information concerning the pressure testing involving hydrogels with an unmodified pipette. | |||
{| {{table}} | |||
| align="center" style="background:#f0f0f0;"|'''Sample Order''' | |||
| align="center" style="background:#f0f0f0;"|'''PVOH vs. Clay Ratio''' | |||
| align="center" style="background:#f0f0f0;"|'''PVOH Type''' | |||
| align="center" style="background:#f0f0f0;"|'''Clay Selection''' | |||
| align="center" style="background:#f0f0f0;"|'''Amount of Hydrogel Used (g)''' | |||
|- | |||
| 1||50:50||130K||110% CEC NaMT w/ DMHXLBR||0.1006 | |||
|- | |||
| 2||50:50||130K||110% CEC NaMT w/ DMHXLBR||0.1022 | |||
|- | |||
| 3||90:10||130K||Laponite||0.1031 | |||
|- | |||
| 4||50:50||146K||110% CEC Laponite w/ DMHXLBR||0.1066 | |||
|- | |||
| 5||90:10||130K||110% CEC Laponite w/ DMHXLBR||0.1083 | |||
|- | |||
| 6||90:10||130K||110% CEC NaMT w/ DMHXLBR||0.1003 | |||
|- | |||
| 7||50:50||130K||110% CEC Laponite w/ DMHXLBR||0.1036 | |||
|- | |||
| 8||50:50||146K||Laponite||0.1016 | |||
|- | |||
| 9||90:10||130K||110% CEC NaMT w/ DMHXLBR||0.1011 | |||
|- | |||
| 10||90:10||146K||110% CEC NaMT w/ DMHXLBR||0.1020 | |||
|- | |||
| 11||50:50||130K||NaMT||0.1024 | |||
|- | |||
| 12||50:50||130K||50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>||0.1015 | |||
|- | |||
| 13||50:50||146K||110% CEC NaMT w/ DMHXLBR||0.0998 | |||
|- | |||
| 14||90:10||130K||50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>||0.1026 | |||
|} | |||
<br> | <br> | ||
Figure 1. Fluorescence of hydrogel samples modified with Lamponite clay using an unmodified pipette for pressure testing | Figure 1. Fluorescence of hydrogel samples modified with Lamponite clay using an unmodified pipette for pressure testing | ||
<br> | |||
Figure 2. Fluorescence of hydrogel samples modified with NaMT clay using an unmodified pipette for pressure testing | Figure 2. Fluorescence of hydrogel samples modified with NaMT clay using an unmodified pipette for pressure testing | ||
<br> | |||
Figure 3. Fluorescence of all hydrogel samples using and unmodified pipette for pressure testing | Figure 3. Fluorescence of all hydrogel samples using and unmodified pipette for pressure testing | ||
<br> | <br> |
Revision as of 07:32, 7 March 2013
Project name | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
Objectives
Pressure tests using an unmodified pipette
Microspheres
|