User:Moira M. Esson/Notebook/CHEM-581/2013/03/22

From OpenWetWare

(Difference between revisions)
Jump to: navigation, search
(Preparation of Microspheres)
(Notes)
Line 45: Line 45:
==Notes==
==Notes==
*Microspheres prepared with PVA 130,000 and PVA 146,000-186,000 will be prepared.
*Microspheres prepared with PVA 130,000 and PVA 146,000-186,000 will be prepared.
 +
*Microspheres prepared on [[User:Moira_M._Esson/Notebook/CHEM-581/2013/03/20|2013/03/20]] seem to have formed small spheres and are easier to vortex as opposed to the previously prepared microsphere samples.

Revision as of 21:07, 24 March 2013

Project name Main project page
Previous entry      Next entry

Objectives

  1. Finish last cycle of rapid freezing and subsequent thawing of the microspheres prepared on 2013/03/20
  2. Preparation of microspheres using PVA MW 130,000
  3. Run two-hour diffusion testing of microspheres with dye added.

Diffusion Testing

  • Diffusion testing was not able to be run. The caps were left on the microsphere samples and the water from the samples had not evaporated. The caps were removed from the samples. Diffusion testing will be completed next class.


Preparation of Microspheres

  • The general protocol for microsphere preparation described on 2013/02/20 and 2013/02/22.
  • The following preparations were run on a 0.05g scale as opposed to a 0.1g scale in case the 0.1g scale forms hydrogels. A comparison of the microspheres prepared on a different gram scale will be made.
  • A very small amount of PVA/clay was added to each vial and the vial was filled with safflower oil prior to the rapid freezing in order to achieve a true emulsion of microspheres in the organic safflower oil. This may prevent the formation of hydrogels.


PVOH vs. Clay Ratio Clay Selection PVOH 146K Mass (g) Actual Clay Mass (g) H2O Added (mL) Dye Concentration (μM)
50:50NaMT0.025300.025302035
50:50Laponite0.025900.025002035
90:10NaMT0.041400.011102035
90:10Laponite0.044700.011002035
50:50110% CEC Laponite0.025500.025002035
90:10110% CEC Laponite0.042300.011502035
50:5050% CEC NaMT0.025400.025002035
90:1050% CEC NaMT0.040100.010502035


Notes

  • Microspheres prepared with PVA 130,000 and PVA 146,000-186,000 will be prepared.
  • Microspheres prepared on 2013/03/20 seem to have formed small spheres and are easier to vortex as opposed to the previously prepared microsphere samples.