User:Moira M. Esson/Notebook/CHEM-581/2013/03/29: Difference between revisions

From OpenWetWare
Jump to navigationJump to search
Line 19: Line 19:
{| {{table}}
{| {{table}}
| align="center" style="background:#f0f0f0;"|'''PVOH MW'''  
| align="center" style="background:#f0f0f0;"|'''PVOH MW'''  
| align="center" style="background:#f0f0f0;"|'''PVOH mass added(g)'''
| align="center" style="background:#f0f0f0;"|'''PVOH Mass(g)'''
|-
| 130,000||0.1040
|-
| 146,000-186,000||0.1022
<br>
*It was noted that the microsphere emulsion prepared with the microspheres containing only PVA appeared to be more white and to have a smoother consistency after blending with safflower oil in comparison to the microsphere emulsions with PVA and clay.




Revision as of 17:50, 30 March 2013

Project name <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page
<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html>&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;</html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>

Objectives

  1. Finish preparation of all microsphere samples.
  2. Finish decanting microsphere samples prepared 2013/03/22.
  3. Dry microsphere samples decanted and rinsed with hexanes(2013/03/27) in preparation for DSC and X-ray.
  4. Consolidate microsphere samples with dye additive and place in new vials in preparation for diffusion testing.


Microsphere Preparation

  • The general protocol for microsphere preparation described on 2013/02/20 and 2013/02/22.
  • A very small amount of PVA/clay was added to each vial and the vial was filled with safflower oil prior to the rapid freezing in order to achieve a true emulsion of microspheres in the organic safflower oil. This may prevent the formation of hydrogels.
  • The four microsphere samples that were dissolved on 2013/03/22 were prepared.
  • It was realized that a microsphere sample without clay additive had not been prepared. Two microsphere samples with only PVA were also prepared.
PVOH MW PVOH Mass(g)
130,000 0.1040
146,000-186,000 0.1022


  • It was noted that the microsphere emulsion prepared with the microspheres containing only PVA appeared to be more white and to have a smoother consistency after blending with safflower oil in comparison to the microsphere emulsions with PVA and clay.
Retrieved from "https://openwetware.org/mediawiki/index.php?title=User:Moira_M._Esson/Notebook/CHEM-581/2013/03/29&oldid=687124"